1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Адхезията на устойчивия на висока температура колан от памучно платно е относително ниска, а адхезията на устойчивия на висока температура EP колан е относително висока; експлоатационният живот на EP устойчивия на висока температура колан е очевидно по-дълъг от този на устойчивия на висока температура колан от памучно платно.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Това е друг метод на залепване, този метод също е възможен, но ако използвате този метод, обърнете внимание на следните точки:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Обикновено, когато температурата на вулканизация е по-висока от критичната температура на вулканизация на ускорителя и вулканизиращия агент и не може да достигне нормалната температура на вулканизация, може да се приеме методът за удължаване на времето за вулканизация, за да може вулканизацията на гумата да отговаря на изискванията. Обикновено всеки път, когато температурата е по-ниска от 10 градуса, времето за вулканизация се удължава с 2-4 пъти. Разбира се, поради съображения за производителност, не препоръчваме използването на ниска{3}}температура и продължителна вулканизация.
5. Can core rubbers from different manufacturers be mixed?
Не се препоръчва смесването на каучук за сърцевина от различни производители, тъй като формулата на каучуковата сърцевина от различни производители е различна. В каучука има много видове смесващи агенти и някои от тях имат интерактивни реакции. Във формулата на един и същ производител няма да има смесващи агенти с нежелани интерактивни реакции, но формулите на различните производители са много различни. Когато се използва, може да има интерактивни отражения на смесващите агенти, които ще повлияят на ефекта от употребата на каучуковата сърцевина.